The Behavior of Cement-Bonded Particleboard with Modified Composition under Static Load Stress

Simple item page
dc.contributor.authorMelichar, Tomášcs
dc.contributor.authorBydžovský, Jiřícs
dc.contributor.authorDvořák, Richardcs
dc.contributor.authorTopolář, Liborcs
dc.contributor.authorKeprdová, Šárkacs
dc.coverage.issue22cs
dc.coverage.volume14cs
dc.date.issued2021-11-10cs
dc.description.abstractThis article presents research on the behavior of cement-bonded particleboards under mechanical stress caused by the static load. The composition of the boards was modified using al-ternative raw materials–dust (DU) forming during the processing of cement-fibre boards and par-ticle mixture (PM) generated in the production of cement-bonded particleboards. The parti-cleboards (1-year-old) were subjected to an adverse environment (100 to 250 frost cycles). Me-chanical parameters were tested, and the development of defects during static load of the boards by bending was analyzed using acoustic emission. Particleboards with modified compositions are slightly more resistant to adverse environments. The results of the acoustic emission showed the different types of defects occurring under stress by bending. Standard-composition particleboards showed defects located mainly under the cylindrical stress-test head. The modified boards showed larger location distribution of the occurring defects that were also concentrated further away from the cylindrical stress head. The energy during the occurrence of defects was higher in the modified boards in the location of weight application than in the reference boards.en
dc.description.abstractČlánek prezentuje výzkum chování cementotřískových desek během jejich mechanického namáhání vyvozeného statickým napětím. Složení desek bylo modifikováno alternativními surovinami. Byl aplikován prach (DU) vznikající při opracování cementotřískových desek – 7 %. Dále byl aplikován vedlejší produkt, což je sypká směs (PM) pro výrobu cementotřískových desek – 8 %. Cílem výzkumu bylo posouzení poruch vznikajících v cementotřískových deskách (stáří 1 rok) vystavených nepříznivému prostředí (mrazuvzdornost – 100 až 250 cyklů). Byla stanovena objemová hmotnost, pevnostní charakteristiky a modul pružnosti. Během statického namáhání desek ohybem byl analyzován vývoj a vznik poruch akustickou emisí (jejich četnost, intenzita v závislosti na síle, lokalitě vzniku atd.). Bylo zjištěno, že desky modifikovaného složení jsou vůči nepříznivému prostředí mírně odolnější, než desky standardního složení. Výsledky akustické emise ukázaly rozdílný způsob vzniku poruch desek během namáhání ohybem. Diference mezi recepturami se s vyšším počtem zmrazovacích a rozmrazovacích cyklů prohlubovaly. Desky standardního složení vykazovaly porušení lokalizované spíše pod válcovou zatěžovací hlavou. Naproti tomu modifikované receptury se při napětí na mezi porušení vyznačovaly větším rozptylem pozice vznikajících poruch, které byly koncentrovány i dále od válcové zatěžovací hlavy. Energie během vzniku poruch v modifikovaných deskách byla v lokalitě zatěžování vyšší než u desek receptury referenční.cs
dc.formattextcs
dc.format.extent1-31cs
dc.format.mimetypeapplication/pdfcs
dc.identifier.citationMaterials . 2021, vol. 14, issue 22, p. 1-31.en
dc.identifier.doi10.3390/ma14226788cs
dc.identifier.issn1996-1944cs
dc.identifier.orcid0000-0003-1132-429Xcs
dc.identifier.orcid0000-0002-4139-2763cs
dc.identifier.orcid0000-0003-0024-2344cs
dc.identifier.orcid0000-0001-9437-473Xcs
dc.identifier.orcid0000-0003-0389-1817cs
dc.identifier.other174976cs
dc.identifier.researcheridAAY-7481-2020cs
dc.identifier.researcheridAAH-5598-2021cs
dc.identifier.researcheridAAL-7858-2020cs
dc.identifier.researcheridE-9341-2018cs
dc.identifier.researcheridKBB-2057-2024cs
dc.identifier.scopus54955810000cs
dc.identifier.scopus25637004500cs
dc.identifier.scopus57195216023cs
dc.identifier.scopus37051376500cs
dc.identifier.scopus55225966100cs
dc.identifier.urihttp://hdl.handle.net/11012/203088
dc.language.isoencs
dc.publisherMDPIcs
dc.relation.ispartofMaterialscs
dc.relation.urihttps://www.mdpi.com/1996-1944/14/22/6788cs
dc.rightsCreative Commons Attribution 4.0 Internationalcs
dc.rights.accessopenAccesscs
dc.rights.sherpahttp://www.sherpa.ac.uk/romeo/issn/1996-1944/cs
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/cs
dc.subjectcement-bonded particleboarden
dc.subjectmodificationen
dc.subjectcompositionen
dc.subjectadverse environmenten
dc.subjectfrosten
dc.subjectstressen
dc.subjectstatic loaden
dc.subjectacoustic emissionen
dc.subjectdefect analysisen
dc.subjectcementotřísková deska
dc.subjectmodifikace
dc.subjectsložení
dc.subjectnepříznivé prostředí
dc.subjectmráz
dc.subjectnamáhání
dc.subjectstatické zatížení
dc.subjectakustická emise
dc.subjectanalýza poruch
dc.titleThe Behavior of Cement-Bonded Particleboard with Modified Composition under Static Load Stressen
dc.title.alternativeChování cementotřískových desek modifikovaného složení při namáhání statickým napětímcs
dc.type.driverarticleen
dc.type.statusPeer-revieweden
dc.type.versionpublishedVersionen
sync.item.dbidVAV-174976en
sync.item.dbtypeVAVen
sync.item.insts2025.02.03 15:45:57en
sync.item.modts2025.01.17 16:47:46en
thesis.grantorVysoké učení technické v Brně. Fakulta stavební. Ústav technologie stavebních hmot a dílcůcs
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
materials1406788v2.pdf
Size:
130.77 MB
Format:
Adobe Portable Document Format
Description:
materials1406788v2.pdf
Download
Collections
Ústav technologie stavebních hmot a dílců