Development of shrinkage and fracture parameters in selected fine-grained cement-based composites

Abstract

The paper summarizes results of a pilot study aimed at the evaluation of an experimental investigation focused on determination of the material characteristics development of selected fine-grained cement-based composites during their ageing. The composition of composites being investigated differed only in a water to cement (w/c) ratio and in amount of superplasticizer. Quite extensive experiments were performed with the aim to determine shrinkage, dynamic a static modulus of elasticity and fracture properties on test specimens exposed to free drying during the whole time of its ageing (including the early stage of setting and hardening). The article presents especially results (including their statistical evaluation) of shrinkage and fracture parameters development within 90 days of composites’ ageing. Experimental results show the dependence of the investigated characteristics on the value of w/c ratio. The most visible effect was observed in the case of shrinkage development. The curing conditions were reflected especially in high variability of the test results.The paper summarizes results of a pilot study aimed at the evaluation of an experimental investigation focused on determination of the material characteristics development of selected fine-grained cement-based composites during their ageing. The composition of composites being investigated differed only in a water to cement (w/c) ratio and in amount of superplasticizer. Quite extensive experiments were performed with the aim to determine shrinkage, dynamic a static modulus of elasticity and fracture properties on test specimens exposed to free drying during the whole time of its ageing (including the early stage of setting and hardening). The article presents especially results (including their statistical evaluation) of shrinkage and fracture parameters development within 90 days of composites’ ageing. Experimental results show the dependence of the investigated characteristics on the value of w/c ratio. The most visible effect was observed in the case of shrinkage development. The curing conditions were reflected especially in high variability of the test results.